The Role of Mixed Graphene/Carbon Nanotubes on the Coating Performance of G/CNTs/Epoxy Resin Nanocomposites
The Role of Mixed Graphene/Carbon Nanotubes on the Coating Performance of G/CNTs/Epoxy Resin Nanocomposites
 
لغة الوثيقة : الانجليزية 
المستخلص : There is no doubt that, epoxy resin is one of the most important materials that has been widely used in coating technology. The present work is aimed to fabricate a new series of epoxy resin nanocomposites in the form of G/CNTs/EPY1-4 using simple dissolution method and ultrasonic assistance. The expected nanocomposites have been fabricated using 10% loading of different mixed ratios from G/CNTs. Four different G/CNTs mixed ratios were used 20/80%, 40/60%, 60/40%, and 80/20%. The structure of the G/CNT/EPY1-4 nanocomposites has been investigated and confirmed by normal characterization techniques including: X-ray diffraction (XRD), Fourier transforms infrared spectroscopy (FT-IR), Thermogravimetric analysis (TGA), Differential Thermal gravimetry (DTG) and field emission scanning electron microscopy (FE-SEM). T-25 and T-50 values for G/CNT/EPY1-4 nanocomposites were slightly higher than elegant epoxy. R-500 values for the fabricated materials were in the range of 8.98-10.04%. Furthermore, the role of mixed G/CNTs on the coating properties of epoxy resin was determined using electrochemical impedance and technique. The coating resistance of epoxy composites in the form of G/CNT/EPY1-4 was larger than that observed for elegant epoxy coating. G/CNT/EPY3 and G/CNT/EPY1 showed highest and the lowest coating impedance values respectively. In addition to that, the water sorption technique has been used as a complementary method for such coating behaviour. The water uptake was efficiently decreased in all the formulations compared to the epoxy due to the presence of G/CNTs reinforcing agents. 
ردمد : 1452-3981 
اسم الدورية : INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE 
المجلد : 11 
العدد : 9 
سنة النشر : 1437 هـ
2016 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Thursday, August 3, 2017 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
M HusseinHussein, M باحث  
B Abu-ZiedAbu-Zied, B باحث  
A AsiriAsiri, A باحث  

الملفات

اسم الملفالنوعالوصف
 42437.pdf pdf 

الرجوع إلى صفحة الأبحاث